| Customization: | Available |
|---|---|
| Application: | Aviation, Electronics, Industrial, Medical, Chemical |
| Standard: | GB, DIN, BS, ASTM, AISI |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Why you choose us? | |||
| 1. more than 20 years experiences in steel business | |||
| 2. good quality | |||
| 3. competitive price | |||
| 4. meet your needs via reprocessing | |||
| 5. excellent service | |||
| 6. short delivery time | |||
| 7. long mutual beneficial business cooperation |
APPLICATION:
2.Widely used in Painting/ Printing/Dyeing/pharmaceutical/rubber industry etc;
3.Chemical industries, zinc and other metal alloy plating coating industry;
4.In zinc plating, manufacture of brass, maganese bronze, galvanized iron, dry battery; as catalyst and reducing agent.
Product Table:
Brand |
Chemical | |||||||||
| Zn(≥) | Impurity(≤) | |||||||||
| Pb | Cd | Fe | Cu | Sn | Al | As | Sb | Totsal | ||
| Zn99.995 | 99.995 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.001 | -- | -- | 0.005 |
| Zn99.99 | 99.99 | 0.005 | 0.003 | 0.003 | 0.002 | 0.001 | 0.002 | -- | -- | 0.01 |
| Zn99.95 | 99.95 | 0.03 | 0.01 | 0.02 | 0.002 | 0.001 | 0.01 | -- | -- | 0.05 |
| Zn99.5 | 99.5 | 0.45 | 0.01 | 0.05 | -- | -- | -- | 0.005 | 0.01 | 0.5 |
| Zn98.5 | 98.5 | 1.4 | 0.01 | 0.05 | -- | -- | -- | -- | -- | 1.5 |
Wholesale High Purity Metal Zinc Ingots 99.995 Price
|
Chemical composition %
|
|||||||||
|
No.
|
Zn
|
Pb
|
Cd
|
Fe
|
Cu
|
Sn
|
Ai
|
As
|
Sb
|
|
Zn99.995
|
>99.995
|
<0.003
|
<0.012
|
<0.001
|
<0.001
|
<0.001
|
_
|
_
|
_
|
USAGE:
1. Mainly used for die-casting alloy battery industry
2. Widely used in Painting/ Printing/Dyeing/pharmaceutical/rubber industry etc.
3. Chemical industries, zinc and other metal alloy plating coating industry
4. In zinc plating, manufacture of brass, maganese bronze, galvanized iron, dry battery; As catalyst and reducing agent.
| ltimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |